BambuLab PET-CF Filament 500g
54,90€ ME ΦΠΑ
Bambu Lab PET-CF filament στο 3DHUB!
Ποιοτικό carbon reinforced αναλώσιμο, με βελτιωμένες μηχανικές ιδιότητες και RFID tag για αυτόματη αναγνώριση στους Bambu 3D Printers!
Διάμετρος: 1.75mm ± 0,03mm Βάρος: 500gr
Product Features
- Very Low Moisture Absorption
- Exceptional Mechanical Properties
- High Dimensional Stability
- Exceptional Thermal Resistance
- Comes with High Temperature Reusable Spool
Cautions for Use
- Dry Out before Use
- AMS Not Compatible
- 0.2 mm Nozzle Not Compatible
Σε απόθεμα (επιπλέον μπορεί να ζητηθεί κατόπιν παραγγελίας)
Bambu PET-CF is a blend of tough PET and carbon fiber. Carbon fiber improves hardness and mechanical strength, while still help maintain the low warping and shrinkage of ordinary PET. Bambu PET-CF has excellent high temperature resistance and a soft glow appearance. Its excellent strength, heat resistance, dimensional stability and low moisture absorption make Bambu PET-CF an ideal choice for load-bearing structures or prints used in high temperature and humid environments.
Low moisture absorption
In saturated water absorption conditions, the strength and stiffness of PET-CF have small losses, making it suitable for prints used in high humidity environments.
Normal PA-CF
Loading Weight: 1 kg
Bambu PET-CF
Loading Weight: 1 kg
The test models have a span of 220 mm and a thickness of 3 mm in unloaded state.
High dimensional stability
Due to the creep and warping resistance of PET-CF, prints can achieve excellent matching accuracy.
Specimens size (L*W*H): 240*8*15 mm³
Infill density: 60%
Exceptional thermal resistance
• Specimen size (L*W*H): 95*10*4 mm³
• Test conditions: Specimens were put in an oven at 70 °C and 150 °C respectively for 0.5 hour.
• As a crystalline material, PLA will significantly deform only after the temperature exceeds its melting point (around 155°C).
Printing setup
0.6 mm Hardened Steel Nozzle (Recommended)
0.4 mm / 0.8 mm Hardened Steel Nozzle (Capable)
Enclosed printer (Recommended)
Open frame printer (Capable)*
AMS NOT compatible
*Layer bonding of some prints may become low due to overcooling.
Accessory Compatibility
Recommended | Not Recommended | |
Build Plate | Engineering Plate, High Temperature Plate or Textured PEI Plate | Cool Plate |
Hotend | Hardened Steel Nozzle(0.4 / 0.6 / 0.8 mm) | Stainless Steel Nozzle (0.2 / 0.4 mm) |
Glue | Glue Stick | Bambu Liquid Glue |
Frequently Asked Questions
What is the difference between PET-CF and PETG-CF?
The primary difference between PET-CF and PETG-CF lies in their base material. PETG-CF is a reinforced material made by adding carbon fiber to glycol-modified polyethylene terephthalate (PETG), while PET-CF is to polyethylene terephthalate (PET). The key difference ‘G‘ in PETG stands for glycol. PETG is a glycol-modified version of PET that contains small amounts of glycol as a co-monomer. The addition of glycol to PETG reduces its crystallinity and makes it more transparent. However, it also reduces its strength and stiffness.
The difference in application between PETG-CF and PET-CF?
PETG-CF is a versatile basic material that is suitable for printing everyday items, such as bent, folded, and movable parts, due to its excellent toughness and ease of printing. PET-CF, in contrast, contains a greater amount of carbon fiber and is significantly stronger and more temperature resistant compared to PETG-CF. PET-CF is a professional-grade engineering material that is suitable for use in more complex and demanding environments.
What is PET-CF used for?
Due to its dimensional stability and lower water absorption rate, PET-CF is a better choice than nylon for printing functional parts used in high humidity environments. Also, its high-temperature resistance and low warping make it suitable for printing mechanical assembly parts, such as automotive accessories and fixtures.
Parameters Comparison
Learn more different filaments comparison on Bambu Filament Guide >>
PET-CF | PAHT-CF | |
Price/1kg | €90.99 | €101.99 |
Composition | PET, carbon fiber | PA 12 and other long-chain PA, carbon fiber |
Hotend Compatibility | Hardened Steel 0.6 (recommended), 0.4, 0.8 mm | |
Build Plate Compatibility | Engineering Plate, High Temperature Plate, Textured PEI Plate | |
Glue | Glue Stick / Liquid Glue | Glue Stick |
AMS Compatibility | NO | Yes |
Print Speed | < 100 mm/s | < 100 mm/s |
Toughness (Impact Strength – XY) | 36.0 kJ/m² | 57.5 kJ/m² |
Strength (Bending Strength – XY) | 131 MPa | 125 MPa |
Stiffness (Bending Modulus – XY) | 5320 MPa | 4230 MPa |
Layer Adhesion (Impact Strength – Z) | 4.5 kJ/m² | 13.3 kJ/m² |
Heat Resistant(HDT, 0.45 MPa) | 205 °C | 194 °C |
Saturated Water Absorption Rate / % (25 °C,55% RH) | 0.37 | 0.88 |
Recommended Printing Settings | |
Drying Settings (Blast Drying Oven) | 80 °C,8 – 12 h |
Printing and Keeping Container’s Humidity | < 20% RH (Sealed,with Desiccant) |
Nozzle Temperature | 260 – 290 °C |
Bed Temperature (with Glue) | 80 – 100 °C |
Printing Speed | < 100 mm/s |
Physical Properties | |
Density | 1.29 g/cm³ |
Vicat Softening Temperature | 226 °C |
Heat Deflection Temperature | 205 °C |
Melting Temperature | 250 °C |
Melt Index | 25.3 ± 2.5 g/10 min |
Mechanical Properties | |
Tensile Strength | 74 ± 6 MPa |
Breaking Elongation Rate | 4.5 ± 1.2 % |
Bending Modulus | 5320 ± 270 MPa |
Bending Strength | 131 ± 6 MPa |
Impact Strength | 36.0 ± 2.7 kJ/m² |
Printing Tips
• Bambu PET-CF needs proper drying before printing: recommended drying temperature is 80 ℃ for 8 hours in a blast drying oven, or 90 ℃ for 10 hours on printer’s heatbed. (Do not exceed 100 ℃ because the spool may melt). For more details, please refer to:Printing tips for Engineering materials on WIKI.
• To prevent the material from absorbing moisture, it is recommended to use an airtight storage container with desiccant during printing. For more details, please refer to:Printing tips for Engineering materials on WIKI.
What’s in the Box
Filament with Spool*1 & Desiccant*1
Filament Label*1
Package*1
Επιπλέον πληροφορίες
Βάρος | 2 kg |
---|---|
Technology | |
Filament Brand | |
Filament Type |