PowerResins Vintage Resin

Developed for directly casting jewelry with great details. Perfect for producing chain models and gourmet series.

Especially suitable for chain models.
Perfect printing properties with sharp details suitable for jewelry with micro-pave prongs, engraving, highly detailed figures or filigree.
Easy to set stones directly on printed model before casting.
Create lighter jewelry with perfect precision.
Perfect 100% ash-free burnout for direct casting.
Use of standard wax burnout cycle.
No need for post-curing after printing

Εξαιρετική χυτευσιμότητα! Έχει πολύ βολικό κύκλο καύσης!

Έρχεται σε μπουκάλι των 500ml. Άμεσα διαθέσιμη!

PowerResins most advanced resin VINTAGE!

VINTAGE resin offers a versatile one-stop solution for all types of jewelry manufacturing needs, offering superb direct casting results with an unseen non-shrinking formula allowing you an easy ash-free resin casting process like a traditional lost wax casting . With VINTAGE resin, compromise is a thing of the past; enjoy smoother surfaces and razor-sharp edges in every print. Additionally, it’s perfectly tailored for intricate stone settings, ensuring precision and quality in every piece.

Shrinkage rate is less than %1
Ash-free casting like a wax
No need post curing
Perfect for stone settings
Find here printing parameters for DLP and LCD printers

Casting and Burnout Cycle for PowerResins Castable Resins

1. Washing the Models

3 minutes with clean alcohol (that is minimum 90% pureness).
Wash 2 minutes with dirty alcohol then dry by blowing air (an air compressor can be used) and then 2 minutes with clean alcohol then dry by blowing air.
Check the models, if there are uncured resin on the model wash and dry them again.
The models should not be exposed to alcohol for more than 6 minutes.
First choice for alcohol; ethyl alcohol is suggested. Otherwise; isopropyl alcohol can be used.
Models should be casted as soon as possible (within 2 hours is suggested). The models must always be stored in a dark and ideally in a sealed plastic bag.

2. Investment Process

Instructions (water-powder ratio, mixing process etc.) by the manufacturer of the investment must be followed.
Must be make sure that the investment gets vacuum very well. The vacuum process must be aplied by vibrating the investment.
Casting tree should be inserted as far away from the surface of the flask as possible (! Do not put the printed model close to the flask’s wall).

Note: Every steps should be completed by the professional machines. Every detail is essential to get applied correctly.

3. Recommended Burnout Cycle

Before insterting the flask into furnace, flask must be left settled for minimum 3 hours.
In the last step of the cycle; after ramp down to 600 Celsius degrees within 1 hour, the flask should stay in the furnace at 600 Celsius degrees for about 1 hour before pouring the metal.
Fresh metal should be used to cast. Metals used for many times (more than 3-4) to get casted should not be used.